Table:NAA data of 139 (incl. 2 repetition measurements) orginating from Euboea and Pendent Semicircle skyphoi ( PSC) from other areas. Concentrations of elements C measured by NAA, University Bonn, in mikrog/g (ppm), if not indicated otherwise, and average errors, also in percent of C Sample factor As Ba Ca% Ce Co Cr Cs Eu Fe% Ga ------------------------------------------------------------------------------------------------------ Chlk 1 1.000 7.15 739. 3.18 79.0 23.5 162. 9.61 1.31 5.21 19.0 Chlk 2 1.000 27.9 700. 3.50 79.1 25.0 162. 10.7 1.36 5.89 27.0 Eret 1 1.000 27.6 720. 3.98 89.8 23.0 133. 7.47 1.59 5.07 22.7 Eret 2 1.000 30.2 451. 5.45 59.9 34.7 541. 21.2 1.21 5.41 16.6 Eret 3 1.000 29.6 706. 4.60 83.0 24.2 153. 10.2 1.49 5.39 21.4 Eret 4 1.000 11.1 736. 3.42 83.3 23.0 153. 9.44 1.53 5.34 23.9 Eret 5 1.000 22.3 475. 6.13 61.2 34.1 554. 20.7 1.24 5.39 19.4 Eret 6 1.000 23.7 662. 3.33 84.4 23.4 156. 8.96 1.51 5.22 18.1 Eret 7 1.000 34.2 695. 3.91 81.9 22.9 154. 8.90 1.55 5.14 22.0 Eret 8 1.000 14.8 672. 3.41 93.5 20.4 129. 7.22 1.61 4.71 22.8 Eret 9 1.000 31.4 687. 3.74 87.4 25.2 170. 7.44 1.52 5.75 30.1 Eret 10 1.000 23.1 653. 3.00 86.5 23.6 155. 9.38 1.52 5.26 34.6 Eret 11 1.000 18.5 684. 3.21 81.1 21.3 145. 9.35 1.40 5.15 24.4 Eret 12 1.000 28.9 713. 3.63 76.3 24.6 152. 10.4 1.39 5.74 29.8 Eret 13 1.000 21.5 667. 3.62 85.8 24.9 165. 9.07 1.51 5.58 24.2 Eret 14 1.000 14.1 664. 3.64 86.9 24.8 165. 8.61 1.55 5.59 27.4 Eret 15 1.000 9.10 658. 3.51 89.0 20.0 136. 7.98 1.59 5.03 24.2 Eret 16 1.000 26.7 672. 3.56 85.6 24.2 161. 10.1 1.51 5.52 26.4 Eret 17 1.000 55.8 622. 3.71 84.4 26.2 169. 7.61 1.46 6.27 25.5 Eret 18 1.000 46.2 778. 3.60 91.2 27.9 194. 7.71 1.58 6.75 29.9 Eret 19 1.000 23.6 829. 3.81 97.6 22.2 138. 6.08 1.65 5.33 29.1 Eret 20 1.000 18.6 817. 3.15 91.6 26.5 172. 9.09 1.57 6.26 34.1 Eret 21 1.000 27.2 787. 4.34 81.3 26.1 173. 10.3 1.41 6.08 24.7 Eret 22 1.000 25.1 717. 3.11 88.0 24.5 161. 9.32 1.47 5.56 30.5 Eret 23 1.000 32.5 827. 3.21 89.5 33.2 174. 7.01 1.59 6.77 31.3 Eret 24 1.000 46.2 749. 5.64 71.0 32.3 331. 8.06 1.24 5.81 21.3 Eret 25 1.000 32.4 838. 3.10 79.6 26.9 174. 11.9 1.35 6.63 33.1 Eret 26 1.000 25.2 786. 5.53 83.6 26.3 283. 9.91 1.39 5.17 26.2 Eret 27 1.000 14.4 777. 3.53 84.7 26.9 175. 10.9 1.46 6.24 34.1 Eret 28 1.000 51.5 801. 3.06 83.4 25.4 172. 10.8 1.49 5.98 27.5 Eret 29 1.000 19.7 740. 3.11 89.5 17.8 119. 7.79 1.52 4.85 28.1 Eret 30 1.000 45.7 748. 3.87 82.6 25.0 162. 11.6 1.49 6.09 28.0 Eret 31 1.000 30.2 766. 3.67 85.5 26.1 166. 10.8 1.53 6.13 30.4 Eret 32 1.000 44.3 778. 3.18 90.2 16.4 119. 7.38 1.60 5.02 35.2 Eret 33 1.000 24.4 717. 3.41 86.7 23.0 160. 10.6 1.44 5.63 34.5 Eret 34 1.000 33.3 748. 5.30 74.4 30.3 268. 10.4 1.29 6.17 29.2 Eret 35 1.000 32.4 640. 7.90 71.0 34.2 332. 9.68 1.23 6.15 27.9 Eret 36 1.000 14.2 733. 3.97 82.5 26.3 169. 11.3 1.42 6.17 34.9 Eret 37 1.000 49.7 685. 4.38 81.7 24.1 162. 10.0 1.45 5.42 28.4 Eret 38 1.000 11.1 723. 4.02 85.7 23.7 152. 9.57 1.50 5.64 32.6 Sample factor As Ba Ca% Ce Co Cr Cs Eu Fe% Ga ------------------------------------------------------------------------------------------------------ Eret 39 1.000 12.1 673. 4.89 78.7 25.6 176. 10.2 1.34 5.60 31.9 Eret 40 1.000 20.4 783. 3.34 81.2 25.6 195. 11.1 1.39 6.12 32.0 Eret 41 1.000 57.4 745. 1.23 73.3 22.3 149. 9.73 1.26 5.82 27.9 Eret 42 1.000 34.8 801. 2.76 77.8 24.7 155. 9.80 1.34 5.80 29.3 Eret 43 1.000 44.9 543. 3.11 78.5 32.2 409. 12.0 1.29 7.11 30.0 Eret 44 1.000 46.9 513. 3.53 88.0 36.2 439. 11.7 1.50 7.02 26.9 Eret 45 1.000 84.5 709. 2.92 80.2 37.8 385. 11.1 1.45 6.93 31.9 Lefk 1 1.000 14.4 677. 4.43 86.4 25.0 167. 9.76 1.45 5.35 27.2 Lefk 2 1.000 23.4 655. 4.43 86.2 25.1 176. 9.57 1.49 5.32 24.3 Lefk 3 1.000 22.9 648. 4.22 71.9 25.7 187. 8.61 1.39 5.17 21.2 Lefk 4 1.000 13.7 694. 4.22 79.4 24.9 157. 11.1 1.40 5.90 30.7 Lefk 5 1.000 19.4 669. 4.51 76.5 26.2 170. 11.1 1.34 5.76 28.7 Lefk 6 1.000 27.1 724. 3.40 78.3 25.5 160. 10.0 1.38 5.84 28.2 Lefk 7 1.000 10.9 781. 2.68 81.8 23.0 160. 9.79 1.35 5.32 25.5 Lefk 8 1.000 7.55 969. 4.19 80.4 23.8 158. 4.46 1.44 5.32 25.4 Lefk 9 1.000 7.58 796. 4.30 85.0 24.7 162. 4.14 1.51 5.48 24.4 Lefk 10 1.000 8.41 714. 3.82 81.5 22.9 146. 9.66 1.40 5.24 26.3 Lefk 11 1.000 25.3 704. 2.76 82.2 24.0 160. 9.90 1.42 5.40 21.3 Lefk 12 1.000 11.8 661. 2.55 74.6 17.9 136. 4.89 1.29 4.83 27.0 Lefk 13 1.000 16.6 293. 1.80 48.1 30.1 614. 4.39 0.65 4.84 13.7 Lefk 14 1.000 14.7 951. 1.17 73.1 13.6 89.8 5.79 1.28 4.28 23.2 Lefk 15 1.000 9.36 989. 3.13 79.0 21.7 148. 9.19 1.32 4.90 24.2 Lefk 16 1.000 4.65 530. 4.48 51.4 24.6 279. 3.90 0.97 4.49 13.7 Lefk 17 1.000 9.48 703. 3.53 87.2 25.4 172. 9.05 1.49 5.46 27.0 Lefk 18 1.000 9.49 696. 4.42 78.8 27.2 180. 11.2 1.41 6.30 34.1 Lefk 19 1.000 14.0 661. 4.03 86.5 25.6 173. 9.74 1.48 5.41 26.6 Lefk 20 1.000 8.00 680. 3.65 83.8 24.4 176. 8.93 1.48 5.32 26.9 Lefk 21 1.000 18.4 746. 3.22 78.4 23.5 164. 10.7 1.41 5.79 23.8 Lefk 22 1.000 15.4 626. 3.67 79.1 24.8 161. 9.07 1.42 5.56 33.0 Lefk 23 1.000 17.4 746. 3.38 83.1 25.9 154. 10.2 1.50 5.72 28.6 Lefk 23 rep. 1.000 18.8 813. 4.86 90.7 27.7 166. 10.8 1.59 6.09 31.4 Lefk 24 1.000 8.11 670. 3.64 83.0 23.9 159. 9.58 1.47 5.30 28.2 Lefk 25 1.000 26.7 718. 4.08 84.8 25.8 165. 10.1 1.47 5.73 23.9 Lefk 26 1.000 32.5 716. 3.89 82.5 25.0 161. 10.2 1.47 5.71 25.9 Lefk 27 1.000 12.1 637. 5.00 81.5 25.0 180. 10.1 1.49 5.80 22.8 Lefk 28 1.000 34.0 686. 3.97 76.4 25.5 166. 11.5 1.37 5.95 36.6 Lefk 31 1.000 24.5 724. 3.95 82.0 23.5 155. 10.5 1.46 5.58 28.3 Lefk 32 1.000 15.4 702. 3.46 79.1 24.7 155. 10.7 1.43 5.98 33.0 Lefk 33 1.000 41.9 532. 5.30 48.6 29.9 549. 5.93 0.91 4.93 11.7 Lefk 34 1.000 24.7 728. 1.91 71.9 19.9 130. 5.94 1.20 4.52 25.7 Sample factor As Ba Ca% Ce Co Cr Cs Eu Fe% Ga ------------------------------------------------------------------------------------------------------ Lefk 35 1.000 19.0 795. 2.02 68.9 20.8 116. 6.19 1.14 4.74 22.3 Lefk 36 1.000 22.4 606. 1.26 79.5 22.0 126. 7.12 1.41 5.05 34.1 Lefk 37 1.000 15.3 661. 4.71 78.1 24.0 142. 7.83 1.57 5.57 18.5 Lefk 38 1.000 18.9 649. 4.47 72.4 21.5 131. 8.76 1.27 4.73 23.7 Lefk 39 1.000 47.2 615. 5.97 77.6 22.1 196. 8.75 1.37 4.94 15.6 Phyl 1 1.000 18.4 428. 0.49 82.7 11.2 219. 7.05 1.25 4.72 20.8 Phyl clay 1 1.000 22.2 439. 10.6 64.6 15.9 98.4 6.19 1.17 3.63 14.8 Phyl clay 2 1.000 25.2 495. 4.90 77.4 20.5 128. 7.00 1.36 4.40 23.5 Orop 1 1.000 20.2 790. 3.74 79.2 24.3 153. 8.95 1.38 5.38 27.0 Orop 2 1.000 9.19 585. 3.74 82.1 26.5 176. 7.63 1.44 5.80 24.5 Orop 3 1.000 16.0 812. 3.04 84.3 25.1 168. 8.64 1.45 5.57 21.7 Orop 4 1.000 19.8 725. 4.09 86.3 26.0 166. 7.86 1.55 5.56 20.0 Orop 5 1.000 20.0 722. 3.62 83.6 26.0 166. 7.87 1.50 5.54 20.7 Orop 6 1.000 17.1 719. 3.41 84.0 24.9 162. 8.31 1.52 5.66 24.4 Orop 7 1.000 14.9 839. 2.55 84.4 25.3 170. 8.11 1.45 5.75 25.6 Orop 8 1.000 24.0 687. 4.99 60.5 34.8 596. 15.4 1.11 5.79 18.5 Orop 9 1.000 11.6 736. 3.52 82.8 25.1 183. 7.55 1.43 5.35 20.0 Orop 10 1.000 15.5 704. 3.03 87.7 25.4 187. 7.95 1.49 5.63 21.3 Orop 11 1.000 24.1 786. 3.34 61.2 35.3 619. 12.2 1.19 5.75 20.8 Orop 12 1.000 18.8 734. 3.25 83.8 23.9 158. 9.32 1.42 5.68 24.1 Orop 13 1.000 20.5 779. 3.77 85.6 24.0 160. 8.15 1.46 5.57 24.7 Orop 14 1.000 19.9 767. 3.29 81.9 23.7 154. 9.45 1.40 5.66 25.2 Ephe 110 1.000 9.96 470. 3.88 87.5 26.8 239. 15.1 1.30 4.53 22.0 Ephe 111 1.000 21.3 845. 4.51 112. 30.4 206. 10.0 1.95 6.49 28.7 Ephe 125 1.000 25.3 645. 3.87 88.1 24.4 156. 9.72 1.49 5.50 33.1 Ephe 143 1.000 8.27 819. 4.30 120. 30.6 189. 10.6 2.00 6.80 41.1 Ephe 162 1.000 34.5 586. 8.04 95.6 24.8 200. 11.0 1.51 5.37 27.5 Ephe 163 1.000 22.5 842. 5.26 108. 30.1 214. 9.95 1.93 6.43 26.2 Ephe 166 1.000 21.3 464. 4.93 87.5 26.4 242. 24.8 1.41 4.79 20.2 Ephe 173 1.000 18.1 571. 4.12 85.0 23.1 153. 10.6 1.43 5.59 31.2 Ephe 179 1.000 29.7 939. 4.73 109. 29.5 198. 10.2 1.85 6.42 32.7 Ephe 205 1.000 34.8 786. 5.80 91.4 34.3 312. 8.58 1.54 5.48 27.4 Ephe 311 1.000 22.8 766. 3.00 81.6 22.2 165. 10.1 1.44 5.21 22.7 Kyme 4 1.000 29.8 656. 3.94 81.3 24.0 159. 10.7 1.45 5.69 -- Kyme 10 1.000 24.9 734. 3.71 80.0 26.3 156. 11.0 1.44 5.86 -- Kyme 11 1.000 11.8 696. 4.07 81.8 27.0 164. 11.6 1.47 6.02 -- VAM 17 6692 1.000 22.0 618. 3.75 103. 24.3 183. 9.27 1.80 5.92 29.1 AlMi 1 1.000 37.0 616. 3.78 83.9 24.9 174. 11.6 1.39 6.11 29.9 AlMi 2 1.000 16.5 631. 4.14 79.7 23.6 157. 10.8 1.38 5.74 30.6 Almi 2 rep. 1.000 16.7 707. 4.36 86.9 24.7 161. 11.3 1.44 5.90 29.2 Sample factor As Ba Ca% Ce Co Cr Cs Eu Fe% Ga ------------------------------------------------------------------------------------------------------ AlMi 3 1.000 18.0 682. 3.99 75.0 24.9 152. 10.0 1.36 5.86 36.7 AlMi 4 1.000 21.8 620. 6.90 65.4 28.9 296. 10.2 1.06 5.95 31.3 AlMi 5 1.000 29.3 693. 3.59 78.4 24.7 167. 10.7 1.38 5.85 26.6 AlMi 6 1.000 25.1 575. 3.91 82.5 24.2 160. 10.6 1.39 5.95 30.7 AlmV 14 1.000 24.2 763. 2.78 76.9 22.5 150. 10.6 1.31 5.48 25.9 AlmV 15 1.000 26.2 677. 2.86 75.0 22.3 150. 9.82 1.33 5.34 22.2 AlmV 17 1.000 38.1 631. 4.97 78.6 18.9 120. 7.04 1.33 4.53 23.3 AlmV 20 1.000 16.5 658. 3.35 75.6 25.0 157. 11.1 1.37 6.02 29.5 AlmV 21 1.000 17.8 636. 2.97 78.9 22.2 150. 9.24 1.41 5.21 25.6 AlmV 23 1.000 29.3 675. 3.73 78.4 24.3 160. 10.6 1.40 5.84 27.2 AlmV 31 1.000 31.9 774. 3.54 82.2 27.2 172. 12.0 1.50 6.49 39.7 Boia 1 1.000 6.95 424. 4.03 86.5 15.7 109. 8.92 1.45 4.28 21.8 Cerv 1 1.000 16.9 866. 2.77 87.2 19.8 150. 11.4 1.35 4.46 36.4 Pont 1 1.000 10.8 538. 3.16 86.3 24.7 163. 10.2 1.60 5.88 39.3 Pont 2 1.000 22.1 809. 2.26 87.2 23.1 163. 10.1 1.53 5.55 26.8 Pont 3 1.000 8.18 363. 6.69 74.9 14.4 129. 6.92 1.40 4.78 24.1 Pont 4 1.000 18.2 667. 3.68 87.5 25.6 171. 10.7 1.51 6.00 42.6 Veji 1 1.000 12.1 712. 2.27 87.9 20.5 150. 12.3 1.36 4.34 33.6 Veji 2 1.000 12.0 829. 2.17 78.1 22.4 153. 11.6 1.73 5.38 31.1 ------------------------------------------------------------------------------------------------------ ave. meas. error 0.14 23. 0.19 0.64 0.14 1.1 0.11 0.026 0.021 2.7 in % 0.6 3.3 4.9 0.8 0.6 0.6 1.1 1.8 0.4 10. Table:NAA data of 139 samples originating from Euboea and PSC skyphoi from other areas. Concentrations of elements C measured by NAA, University Bonn, in mikrog/g (ppm), if not indicated otherwise, and average errors, also in percent of C Sample factor Hf K % La Lu Na% Nd Ni Rb Sb Sc ------------------------------------------------------------------------------------------------------ Chlk 1 1.000 4.88 3.18 36.6 0.48 1.20 31.9 184. 160. 2.21 21.7 Chlk 2 1.000 4.25 3.50 38.0 0.48 0.88 32.2 129. 174. 2.65 23.9 Eret 1 1.000 5.72 3.15 43.7 0.54 1.25 36.9 77.3 156. 2.59 21.8 Eret 2 1.000 4.31 2.36 29.0 0.47 0.60 26.8 450. 143. 0.98 23.7 Eret 3 1.000 4.83 3.31 40.5 0.50 1.05 32.6 190. 165. 2.38 22.5 Eret 4 1.000 5.29 3.21 40.2 0.53 1.09 35.3 136. 166. 2.53 22.3 Eret 5 1.000 4.40 2.53 28.8 0.48 0.62 26.3 371. 134. 1.00 23.6 Eret 6 1.000 5.26 3.20 40.1 0.53 1.18 34.0 148. 157. 2.07 21.7 Eret 7 1.000 5.08 3.14 39.8 0.53 1.18 36.4 152. 154. 2.17 21.6 Eret 8 1.000 6.59 3.28 44.8 0.57 1.45 38.4 143. 161. 2.59 20.8 Eret 9 1.000 5.30 2.94 41.3 0.51 1.09 34.2 144. 138. 2.27 22.3 Eret 10 1.000 5.35 3.30 40.9 0.52 1.12 35.4 154. 157. 2.36 21.7 Eret 11 1.000 4.65 3.32 38.8 0.49 1.11 32.3 109. 172. 2.70 21.8 Eret 12 1.000 4.06 3.48 36.4 0.47 0.85 30.2 180. 173. 2.49 23.3 Eret 13 1.000 5.57 3.25 40.7 0.52 1.20 36.2 217. 153. 2.12 22.4 Eret 14 1.000 5.02 3.02 41.6 0.55 1.05 35.4 95.4 149. 2.53 22.4 Eret 15 1.000 5.52 3.40 43.1 0.54 1.31 36.1 167. 161. 2.43 21.8 Eret 16 1.000 5.00 3.24 40.4 0.51 1.15 34.7 165. 166. 2.42 22.6 Eret 17 1.000 4.52 2.98 40.1 0.54 0.85 34.2 220. 143. 2.06 22.8 Eret 18 1.000 5.01 2.98 43.3 0.55 0.87 39.7 191. 137. 2.41 25.5 Eret 19 1.000 6.21 2.98 45.8 0.56 1.30 44.5 164. 131. 2.78 21.5 Eret 20 1.000 4.66 3.26 43.1 0.54 0.96 39.3 189. 156. 3.55 24.6 Eret 21 1.000 4.26 3.25 38.9 0.49 1.14 37.0 182. 163. 2.66 24.6 Eret 22 1.000 5.22 3.11 41.2 0.50 1.09 38.8 190. 161. 2.42 22.4 Eret 23 1.000 4.37 3.19 41.9 0.57 0.86 40.5 167. 143. 2.97 25.7 Eret 24 1.000 4.61 3.13 33.1 0.46 0.60 29.7 386. 149. 1.97 22.9 Eret 25 1.000 3.96 3.80 37.5 0.52 0.72 34.2 216. 191. 3.23 26.4 Eret 26 1.000 5.39 3.22 39.5 0.51 0.77 37.6 297. 169. 2.00 23.8 Eret 27 1.000 4.42 3.60 39.8 0.51 0.92 35.0 125. 178. 2.63 25.2 Eret 28 1.000 4.45 3.59 39.7 0.52 0.90 37.5 184. 178. 2.56 24.3 Eret 29 1.000 5.99 4.02 42.5 0.56 1.24 39.6 90.4 197. 3.19 24.4 Eret 30 1.000 4.23 3.53 39.3 0.50 1.00 34.9 186. 174. 2.90 24.9 Eret 31 1.000 4.46 3.53 40.9 0.48 1.01 37.1 175. 180. 2.71 25.2 Eret 32 1.000 5.88 3.98 43.1 0.59 1.06 40.5 149. 195. 3.22 23.9 Eret 33 1.000 4.74 3.47 40.9 0.50 1.07 37.7 211. 171. 2.65 23.5 Eret 34 1.000 4.47 3.30 35.5 0.51 0.71 32.3 321. 166. 2.36 24.5 Eret 35 1.000 4.74 1.57 32.9 0.46 1.42 31.7 400. 99.3 2.13 24.9 Eret 36 1.000 4.22 3.52 38.7 0.51 0.87 33.5 201. 185. 2.88 25.1 Eret 37 1.000 4.69 3.10 38.9 0.52 1.09 35.6 220. 160. 2.09 22.4 Eret 38 1.000 5.02 3.31 41.3 0.55 1.03 36.9 144. 173. 2.56 23.8 Sample factor Hf K % La Lu Na% Nd Ni Rb Sb Sc ------------------------------------------------------------------------------------------------------ Eret 39 1.000 4.46 3.26 37.4 0.50 0.97 34.3 177. 162. 2.41 23.0 Eret 40 1.000 4.35 3.73 38.2 0.50 0.87 34.1 192. 181. 2.74 24.9 Eret 41 1.000 4.33 4.00 33.9 0.48 1.01 29.4 135. 173. 2.80 22.7 Eret 42 1.000 3.92 3.80 36.3 0.47 0.89 32.5 89.2 167. 2.44 23.3 Eret 43 1.000 5.98 3.20 36.8 0.49 0.58 31.1 362. 163. 3.27 24.8 Eret 44 1.000 6.30 2.89 42.2 0.54 0.45 40.2 426. 159. 3.55 26.1 Eret 45 1.000 5.31 3.02 39.1 0.54 0.48 34.2 378. 161. 3.76 25.8 Lefk 1 1.000 4.77 3.33 40.1 0.56 1.22 34.3 189. 156. 2.48 22.0 Lefk 2 1.000 4.88 3.12 40.3 0.53 1.06 35.8 195. 158. 2.41 21.7 Lefk 3 1.000 4.36 2.78 34.7 0.45 1.24 30.1 175. 146. 2.51 21.7 Lefk 4 1.000 4.13 3.30 38.3 0.47 0.91 32.7 160. 177. 2.72 24.4 Lefk 5 1.000 4.11 3.13 37.4 0.50 0.80 30.0 226. 172. 2.74 23.8 Lefk 6 1.000 4.16 3.40 37.7 0.47 1.03 33.6 126. 174. 2.76 24.1 Lefk 7 1.000 5.13 3.08 38.3 0.49 1.19 32.3 156. 165. 2.50 22.4 Lefk 8 1.000 5.16 2.37 39.3 0.51 0.95 33.4 168. 94.8 1.89 21.3 Lefk 9 1.000 5.29 2.54 41.4 0.50 1.03 35.9 187. 94.4 1.68 21.7 Lefk 10 1.000 4.80 3.04 39.7 0.49 1.21 34.8 155. 160. 2.55 22.0 Lefk 11 1.000 4.81 3.07 39.0 0.49 1.02 33.1 -- 157. 2.72 22.1 Lefk 12 1.000 4.79 2.25 35.1 0.45 0.60 29.9 95.6 126. 1.10 19.9 Lefk 13 1.000 4.54 1.14 22.3 0.29 0.37 18.4 673. 70.8 1.11 13.7 Lefk 14 1.000 6.43 2.64 37.0 0.44 0.66 30.6 109. 144. 1.70 17.4 Lefk 15 1.000 4.72 3.20 38.3 0.47 1.16 31.6 180. 154. 1.98 20.4 Lefk 16 1.000 4.51 1.92 24.5 0.39 1.60 20.3 249. 88.7 0.55 18.4 Lefk 17 1.000 5.12 3.01 41.7 0.51 1.15 35.4 161. 156. 2.36 22.5 Lefk 18 1.000 3.96 3.54 37.8 0.52 0.82 33.0 177. 182. 2.84 25.7 Lefk 19 1.000 5.27 2.92 40.6 0.50 1.05 34.0 216. 154. 2.43 22.1 Lefk 20 1.000 5.57 3.00 39.2 0.51 1.12 33.9 152. 147. 2.13 21.8 Lefk 21 1.000 4.20 3.56 38.7 0.50 0.75 33.2 182. 178. 2.56 25.0 Lefk 22 1.000 4.61 3.81 37.0 0.50 1.48 34.7 80.9 159. 2.56 23.2 Lefk 23 1.000 4.47 3.38 40.1 0.55 1.04 36.0 154. 170. 2.65 24.0 Lefk 23 rep. 1.000 4.80 3.68 42.7 0.56 1.08 36.8 145. 188. 2.64 25.5 Lefk 24 1.000 5.20 3.16 39.9 0.54 1.26 34.7 177. 155. 2.53 22.1 Lefk 25 1.000 4.44 3.52 40.3 0.50 1.05 35.0 120. 169. 2.87 23.8 Lefk 26 1.000 4.48 3.63 39.8 0.52 1.11 35.4 200. 169. 2.72 23.7 Lefk 27 1.000 4.58 3.23 38.9 0.52 1.17 33.4 195. 155. 2.77 23.8 Lefk 28 1.000 4.15 3.20 36.9 0.48 0.89 31.4 240. 180. 2.73 24.3 Lefk 31 1.000 4.16 3.32 39.3 0.49 0.98 33.4 135. 182. 2.50 23.4 Lefk 32 1.000 3.88 3.51 38.4 0.51 0.89 32.6 101. 177. 2.51 24.6 Lefk 33 1.000 2.98 2.15 25.3 0.30 0.87 19.0 370. 101. 1.20 19.4 Lefk 34 1.000 4.60 2.46 34.0 0.42 0.90 27.1 178. 122. 1.60 17.5 Sample factor Hf K % La Lu Na% Nd Ni Rb Sb Sc ------------------------------------------------------------------------------------------------------ Lefk 35 1.000 4.97 2.36 31.3 0.46 0.88 25.3 147. 129. 1.98 17.9 Lefk 36 1.000 5.88 2.90 39.0 0.54 0.91 33.7 71.2 145. 1.89 20.4 Lefk 37 1.000 4.84 2.75 37.3 0.50 1.17 33.0 137. 138. 1.85 22.5 Lefk 38 1.000 4.04 2.84 34.3 0.42 0.87 27.9 135. 156. 1.60 19.5 Lefk 39 1.000 4.44 2.98 37.6 0.50 1.05 31.5 130. 143. 2.26 20.6 Phyl 1 1.000 6.84 2.04 38.4 0.44 0.70 31.8 116. 119. 1.99 17.8 Phyl clay 1 1.000 3.77 2.15 31.3 0.39 0.98 25.8 92.8 107. 1.82 15.3 Phyl clay 2 1.000 4.92 2.51 36.3 0.50 1.24 31.0 137. 127. 2.07 18.9 Orop 1 1.000 4.86 2.94 38.3 0.51 1.07 33.9 170. 149. 2.57 21.3 Orop 2 1.000 5.34 2.81 39.5 0.51 1.08 31.8 194. 131. 2.26 21.8 Orop 3 1.000 5.58 2.79 39.7 0.53 1.01 35.5 214. 137. 2.35 21.4 Orop 4 1.000 5.53 2.84 41.1 0.51 1.13 36.5 206. 135. 2.40 22.0 Orop 5 1.000 5.36 2.91 39.7 0.53 1.12 35.7 184. 137. 2.40 21.8 Orop 6 1.000 5.09 2.96 40.3 0.49 1.00 35.2 198. 142. 2.46 22.1 Orop 7 1.000 5.40 2.86 39.8 0.55 0.98 35.8 266. 139. 2.64 21.6 Orop 8 1.000 4.51 2.10 27.6 0.42 0.57 25.0 465. 122. 1.10 24.2 Orop 9 1.000 5.67 2.61 39.4 0.52 1.03 34.5 188. 127. 2.04 20.9 Orop 10 1.000 5.78 2.75 40.9 0.53 1.08 37.5 183. 134. 2.32 22.2 Orop 11 1.000 4.47 1.77 27.1 0.47 0.41 25.8 499. 95.5 0.96 25.3 Orop 12 1.000 4.86 3.14 39.2 0.52 0.98 32.5 119. 157. 2.50 22.7 Orop 13 1.000 5.14 2.81 40.0 0.51 1.02 34.5 157. 137. 2.60 21.7 Orop 14 1.000 4.90 3.11 39.0 0.51 0.98 32.3 223. 157. 2.59 22.5 Ephe 110 1.000 5.86 2.72 41.1 0.51 1.03 30.4 233. 158. 2.16 17.3 Ephe 111 1.000 6.23 3.29 52.1 0.66 1.17 48.6 184. 155. 2.67 22.9 Ephe 125 1.000 4.84 3.40 40.3 0.53 1.09 31.0 167. 168. 2.64 22.9 Ephe 143 1.000 6.04 3.36 54.1 0.65 1.10 50.5 182. 168. 3.21 25.0 Ephe 162 1.000 4.05 3.23 43.9 0.50 0.57 43.1 231. 196. 2.91 19.4 Ephe 163 1.000 5.65 3.11 49.3 0.59 1.07 51.6 169. 152. 2.89 24.2 Ephe 166 1.000 5.63 2.80 41.0 0.49 0.73 32.4 213. 166. 2.08 18.5 Ephe 173 1.000 4.28 3.59 38.9 0.50 0.86 31.7 144. 173. 2.69 23.0 Ephe 179 1.000 5.27 3.30 50.9 0.57 1.23 48.9 189. 164. 3.30 24.1 Ephe 205 1.000 4.94 2.86 42.4 0.53 1.04 36.1 328. 134. 2.62 21.7 Ephe 311 1.000 4.55 3.64 38.0 0.49 1.15 33.8 153. 168. 2.05 22.0 Kyme 4 1.000 4.07 3.64 39.3 0.50 0.89 33.7 125. 177. 2.85 23.7 Kyme 10 1.000 4.22 3.68 38.6 0.50 0.94 31.7 68.8 181. 2.77 24.2 Kyme 11 1.000 4.06 3.64 38.4 0.58 0.84 31.1 92.4 187. 2.96 24.9 VAM 17 6692 1.000 4.69 2.83 47.3 0.57 1.04 39.3 208. 141. 1.85 20.4 AlMi 1 1.000 4.14 3.67 38.6 0.62 0.79 32.4 157. 177. 3.39 24.9 AlMi 2 1.000 4.11 3.63 39.1 0.46 0.96 32.4 259. 183. 3.75 23.8 Almi 2 rep. 1.000 4.49 3.60 39.6 0.53 0.95 33.6 112. 182. 2.83 24.6 Sample factor Hf K % La Lu Na% Nd Ni Rb Sb Sc ------------------------------------------------------------------------------------------------------ AlMi 3 1.000 3.87 3.48 36.7 0.45 0.87 27.0 131. 178. 3.33 23.6 AlMi 4 1.000 4.27 3.59 31.0 0.47 0.52 24.7 237. 170. 2.26 25.3 AlMi 5 1.000 4.05 3.79 38.0 0.50 0.88 30.8 138. 185. 3.16 24.4 AlMi 6 1.000 4.30 3.81 39.1 0.45 0.90 32.9 164. 181. 2.90 24.6 AlmV 14 1.000 4.26 3.56 37.0 0.48 0.90 34.1 152. 178. 2.60 23.4 AlmV 15 1.000 4.17 3.45 35.7 0.48 0.87 33.7 114. 157. 2.49 22.3 AlmV 17 1.000 5.19 3.37 37.6 0.47 1.20 33.5 128. 153. 5.92 19.9 AlmV 20 1.000 3.83 3.64 36.8 0.47 0.75 34.3 114. 171. 2.80 24.5 AlmV 21 1.000 4.58 3.36 38.0 0.50 1.00 34.9 109. 162. 2.37 21.6 AlmV 23 1.000 4.24 3.64 38.0 0.55 0.93 32.2 150. 177. 2.52 23.9 AlmV 31 1.000 4.39 3.87 39.8 0.58 0.81 32.8 147. 188. 2.80 26.4 Boja 1 1.000 5.82 2.42 47.3 0.47 0.81 37.3 137. 173. 0.67 14.6 Cerv 1 1.000 4.38 3.26 38.6 0.48 1.11 30.6 139. 183. 3.25 21.1 Pont 1 1.000 4.35 3.51 55.2 0.61 0.88 34.4 247. 179. 2.89 23.3 Pont 2 1.000 5.06 3.43 49.1 0.54 0.80 39.9 170. 173. 2.52 21.4 Pont 3 1.000 4.36 2.52 45.9 0.43 0.69 33.3 61.6 146. 0.65 16.1 Pont 4 1.000 4.56 3.71 40.7 0.59 1.03 34.1 255. 183. 2.67 24.8 Veji 1 1.000 4.54 3.63 38.4 0.48 0.99 30.7 91.0 207. 2.26 22.4 Veji 2 1.000 4.05 3.32 45.6 0.60 0.69 38.3 190. 195. 2.85 22.3 ------------------------------------------------------------------------------------------------------ ave. meas. error 0.069 0.037 0.11 0.018 0.006 1.1 37. 3.1 0.10 0.027 in % 1.4 1.2 0.3 3.5 0.6 3.2 20. 2.0 4.1 0.1 Table:NAA data of 139 samples originating from Euboea and PSC skyphoi from other areas. Concentrations of elements C measured by NAA, University Bonn, in mikrog/g (ppm), if not indicated otherwise, and average errors, also in percent of C Sample factor Sm Ta Tb Th U W Yb Zn ------------------------------------------------------------------------------------------------------ Chlk 1 1.000 6.33 1.07 0.79 14.1 1.68 2.86 2.97 -- Chlk 2 1.000 6.21 1.08 0.78 14.9 2.27 3.76 3.11 122. Eret 1 1.000 7.33 1.11 1.03 15.7 2.55 3.75 3.59 116. Eret 2 1.000 5.34 0.78 0.71 9.95 2.21 2.01 3.11 128. Eret 3 1.000 6.65 1.08 0.92 14.7 2.70 3.72 3.32 121. Eret 4 1.000 6.64 1.04 0.82 14.7 2.29 3.33 3.35 113. Eret 5 1.000 5.21 0.81 0.68 10.0 2.01 2.01 2.86 163. Eret 6 1.000 6.65 1.00 0.93 14.4 2.64 3.39 3.40 117. Eret 7 1.000 6.59 0.98 0.95 14.1 3.02 3.24 3.56 148. Eret 8 1.000 7.49 1.16 1.10 15.5 2.40 3.32 3.69 105. Eret 9 1.000 6.61 1.15 0.99 15.6 2.54 3.11 3.52 117. Eret 10 1.000 6.75 1.07 0.91 15.0 2.53 3.69 3.45 109. Eret 11 1.000 6.27 1.10 0.84 14.5 2.42 4.35 3.24 112. Eret 12 1.000 6.14 1.03 0.81 14.6 2.27 4.23 3.12 126. Eret 13 1.000 6.58 1.11 0.86 15.0 2.42 3.02 3.50 117. Eret 14 1.000 6.78 1.08 0.97 15.3 2.56 2.96 3.45 120. Eret 15 1.000 7.05 1.18 0.96 15.6 2.34 3.24 3.57 114. Eret 16 1.000 6.61 1.04 0.82 15.0 3.10 3.20 3.42 117. Eret 17 1.000 6.49 1.13 0.85 15.6 2.81 4.23 3.33 132. Eret 18 1.000 7.48 1.20 0.86 17.4 3.14 3.62 3.42 147. Eret 19 1.000 8.48 1.23 1.00 16.8 2.04 3.04 3.82 121. Eret 20 1.000 7.60 1.14 0.90 17.1 2.43 3.24 3.36 156. Eret 21 1.000 6.93 1.02 0.84 15.8 2.30 2.98 3.04 132. Eret 22 1.000 7.38 1.10 0.92 15.7 2.38 2.62 3.42 112. Eret 23 1.000 7.70 1.14 0.96 17.2 2.44 3.87 3.60 140. Eret 24 1.000 5.62 0.98 0.65 13.5 2.56 2.05 2.89 97.0 Eret 25 1.000 6.54 1.09 0.82 16.5 2.38 3.81 3.03 134. Eret 26 1.000 6.73 1.03 0.79 15.2 2.98 2.20 3.32 100. Eret 27 1.000 6.98 1.08 0.79 16.0 2.43 3.02 3.29 135. Eret 28 1.000 7.00 1.07 0.86 15.3 2.75 3.50 3.26 112. Eret 29 1.000 7.69 1.23 1.01 17.4 2.42 3.90 3.65 117. Eret 30 1.000 6.67 1.00 0.83 15.5 2.66 3.41 3.18 125. Eret 31 1.000 6.91 1.06 0.82 15.6 2.50 3.37 3.31 126. Eret 32 1.000 7.65 1.24 1.00 17.2 2.38 3.74 3.91 112. Eret 33 1.000 6.99 1.07 0.85 15.4 2.48 3.92 3.43 107. Eret 34 1.000 5.98 1.02 0.82 14.9 2.44 2.66 3.02 124. Eret 35 1.000 5.70 1.02 0.68 14.0 3.17 1.83 2.71 112. Eret 36 1.000 6.39 1.10 0.81 16.1 2.52 3.69 3.25 133. Eret 37 1.000 6.61 1.07 0.87 14.1 2.84 3.15 3.25 95.7 Eret 38 1.000 6.99 1.11 0.90 15.9 2.48 3.46 3.41 144. Sample factor Sm Ta Tb Th U W Yb Zn ------------------------------------------------------------------------------------------------------ Eret 39 1.000 6.13 1.02 0.81 14.7 2.32 3.21 3.08 162. Eret 40 1.000 6.31 1.14 0.82 15.5 2.50 3.78 3.19 106. Eret 41 1.000 5.55 1.11 0.71 15.0 2.88 4.04 3.02 121. Eret 42 1.000 6.12 1.03 0.73 14.9 2.60 4.03 2.95 124. Eret 43 1.000 5.76 1.30 0.69 14.9 2.91 4.52 3.06 107. Eret 44 1.000 6.95 1.31 0.85 16.7 3.14 4.52 3.43 111. Eret 45 1.000 6.52 1.23 0.81 16.4 3.00 4.26 3.07 117. Lefk 1 1.000 6.65 1.10 0.98 14.3 2.34 3.88 3.48 108. Lefk 2 1.000 6.70 1.00 0.92 14.3 2.40 -- 3.39 117. Lefk 3 1.000 6.15 0.95 0.81 12.8 2.07 2.90 2.97 126. Lefk 4 1.000 6.49 0.94 0.81 15.2 2.30 3.16 3.07 131. Lefk 5 1.000 6.20 1.04 0.89 14.3 2.14 2.90 3.01 118. Lefk 6 1.000 6.49 1.00 0.84 15.3 2.21 3.10 3.24 119. Lefk 7 1.000 6.47 1.09 0.87 14.9 2.24 3.42 3.19 113. Lefk 8 1.000 6.62 1.43 0.86 14.7 2.26 2.87 3.31 111. Lefk 9 1.000 6.87 1.14 0.99 15.1 2.23 3.15 3.45 123. Lefk 10 1.000 6.68 1.01 1.01 14.3 2.34 3.25 3.32 118. Lefk 11 1.000 6.57 1.05 1.04 14.3 2.23 3.63 3.16 117. Lefk 12 1.000 5.93 0.92 0.87 13.4 1.66 2.46 3.03 96.8 Lefk 13 1.000 3.12 0.73 0.39 10.3 1.29 2.05 1.78 54.3 Lefk 14 1.000 5.87 1.07 0.82 19.6 2.26 2.94 3.24 86.8 Lefk 15 1.000 6.08 1.05 0.90 13.5 2.66 2.65 3.15 112. Lefk 16 1.000 4.21 0.72 0.73 9.61 1.38 2.09 2.65 72.3 Lefk 17 1.000 6.95 1.05 1.02 15.1 2.57 2.87 3.54 110. Lefk 18 1.000 6.24 0.97 0.78 15.8 2.34 3.19 3.19 139. Lefk 19 1.000 6.57 1.03 0.94 14.6 2.32 3.28 3.34 109. Lefk 20 1.000 6.35 1.04 0.93 14.6 2.21 2.65 3.37 109. Lefk 21 1.000 6.17 1.01 0.86 15.0 2.21 3.89 3.14 119. Lefk 22 1.000 6.27 1.02 0.84 14.9 2.31 3.58 3.20 125. Lefk 23 1.000 6.70 1.02 0.93 14.8 2.60 3.65 3.50 118. Lefk 23 rep. 1.000 7.19 1.22 1.11 15.9 2.58 3.29 3.61 123. Lefk 24 1.000 6.65 1.06 0.95 14.7 2.39 3.58 3.37 121. Lefk 25 1.000 6.54 0.94 1.01 15.1 2.20 3.79 3.27 125. Lefk 26 1.000 6.40 0.99 0.91 15.0 2.16 3.64 3.22 111. Lefk 27 1.000 6.20 1.00 0.87 14.6 2.10 3.30 3.33 126. Lefk 28 1.000 6.06 1.02 0.83 15.4 2.44 3.61 3.08 127. Lefk 31 1.000 6.40 1.04 0.97 14.8 2.26 3.75 3.14 119. Lefk 32 1.000 6.17 1.02 0.85 14.8 2.31 4.14 3.22 125. Lefk 33 1.000 3.38 0.64 0.56 9.29 1.81 2.06 1.88 73.8 Lefk 34 1.000 5.18 0.94 0.89 13.1 2.12 2.91 2.94 90.5 Sample factor Sm Ta Tb Th U W Yb Zn ------------------------------------------------------------------------------------------------------ Lefk 35 1.000 5.04 1.00 0.80 12.7 2.24 3.56 3.04 97.8 Lefk 36 1.000 6.40 1.15 0.90 16.1 2.31 3.38 3.67 88.9 Lefk 37 1.000 6.35 1.13 0.95 12.6 2.24 3.66 3.37 113. Lefk 38 1.000 5.39 0.89 0.72 12.6 2.14 3.52 2.85 104. Lefk 39 1.000 5.88 0.95 0.95 13.2 2.13 3.39 3.25 108. Phyl 1 1.000 5.72 1.23 0.78 15.0 2.19 3.55 3.22 82.4 Phyl clay 1 1.000 4.77 0.77 0.75 10.6 1.96 2.83 2.81 76.5 Phyl clay 2 1.000 5.88 0.89 0.92 12.4 2.44 3.31 3.34 90.5 Orop 1 1.000 6.51 1.07 0.86 14.5 2.26 3.39 3.18 113. Orop 2 1.000 6.02 1.10 0.93 14.6 2.12 2.65 3.40 139. Orop 3 1.000 6.87 1.12 0.84 14.9 2.12 3.23 3.36 105. Orop 4 1.000 7.11 1.10 0.99 15.1 2.03 2.48 3.49 114. Orop 5 1.000 6.86 1.10 0.94 15.0 2.30 2.58 3.33 112. Orop 6 1.000 6.82 1.10 0.86 15.1 2.05 3.10 3.31 117. Orop 7 1.000 6.63 1.11 0.87 15.3 2.27 3.40 3.51 108. Orop 8 1.000 5.15 0.82 0.75 10.3 2.05 2.06 2.88 115. Orop 9 1.000 6.53 1.08 0.87 14.4 2.21 2.80 3.48 104. Orop 10 1.000 6.98 1.14 0.94 15.2 2.38 3.28 3.57 106. Orop 11 1.000 5.16 0.84 0.67 10.7 2.12 2.31 2.95 121. Orop 12 1.000 6.41 1.07 0.81 15.0 2.32 3.69 3.31 108. Orop 13 1.000 6.69 1.10 0.89 15.3 2.22 3.22 3.40 112. Orop 14 1.000 6.46 1.10 0.88 14.9 2.19 3.77 3.31 106. Ephe 110 1.000 6.48 1.33 1.00 18.7 3.02 2.15 3.56 91.0 Ephe 111 1.000 9.81 1.02 1.30 17.2 2.94 2.33 4.43 129. Ephe 125 1.000 6.18 0.95 0.91 14.8 2.48 3.91 3.38 103. Ephe 143 1.000 9.73 1.04 1.23 17.9 3.20 2.26 4.09 148. Ephe 162 1.000 7.72 1.17 1.09 18.6 2.75 2.81 3.44 106. Ephe 163 1.000 10.1 0.94 1.20 16.7 2.51 2.48 3.97 132. Ephe 166 1.000 6.09 1.23 0.89 16.9 2.79 2.90 3.33 117. Ephe 173 1.000 6.15 1.01 0.88 14.8 2.35 3.93 3.19 120. Ephe 179 1.000 10.2 0.92 1.23 16.8 3.38 2.51 4.02 123. Ephe 205 1.000 7.01 0.81 1.00 15.2 2.94 2.85 3.41 112. Ephe 311 1.000 6.39 1.05 0.88 14.0 2.76 2.76 3.20 97.1 Kyme 4 1.000 6.16 1.07 0.86 14.6 2.67 3.31 3.08 112. Kyme 10 1.000 5.70 1.09 0.82 15.0 2.49 4.24 3.18 122. Kyme 11 1.000 5.94 1.06 0.91 15.4 2.42 4.07 3.16 130. VAM 17 6692 1.000 7.80 0.91 1.10 16.3 2.32 2.31 3.66 -- AlMi 1 1.000 6.10 1.05 0.92 16.1 2.72 3.98 3.17 126. AlMi 2 1.000 6.13 0.95 0.69 14.9 2.62 3.36 3.15 78.9 Almi 2 rep. 1.000 6.40 1.06 0.80 15.5 2.51 2.92 3.28 131. Sample factor Sm Ta Tb Th U W Yb Zn ------------------------------------------------------------------------------------------------------ AlMi 3 1.000 5.65 0.97 0.65 14.4 2.48 3.44 2.99 66.8 AlMi 4 1.000 4.75 0.94 0.74 13.8 3.23 2.78 2.76 57.1 AlMi 5 1.000 5.98 0.98 1.09 15.2 2.49 4.21 3.22 75.5 AlMi 6 1.000 6.14 1.04 1.26 15.2 2.48 4.10 3.26 65.8 AlmV 14 1.000 6.38 0.95 0.75 14.6 2.93 3.67 3.07 115. AlmV 15 1.000 6.22 0.94 0.69 13.9 1.86 3.37 3.18 112. AlmV 17 1.000 6.48 1.05 0.84 13.5 2.22 3.73 3.13 91.8 AlmV 20 1.000 6.25 1.09 0.66 15.1 2.75 2.94 3.04 132. AlmV 21 1.000 6.55 1.02 0.78 13.9 2.12 3.66 3.25 111. AlmV 23 1.000 6.51 0.95 0.88 15.0 2.19 4.10 3.16 113. AlmV 31 1.000 6.53 1.09 0.87 16.4 2.53 4.10 3.36 140. Boja 1 1.000 6.61 1.34 0.88 15.9 2.58 2.75 3.00 102. Cerv 1 1.000 5.49 1.04 0.80 14.7 2.61 4.41 3.02 117. Pont 1 1.000 5.96 1.16 1.02 15.6 2.23 4.52 3.23 149. Pont 2 1.000 7.07 1.11 1.00 15.3 2.42 3.36 3.51 124. Pont 3 1.000 5.86 1.16 0.80 12.9 2.76 3.28 2.81 103. Pont 4 1.000 6.09 1.05 0.91 15.7 2.61 5.08 3.32 159. Veji 1 1.000 5.78 1.01 0.91 15.5 2.43 4.11 3.07 110. Veji 2 1.000 7.01 1.05 1.00 14.6 3.26 3.47 3.81 109. -------------------------------------------------------------------------------------- ave. meas. error 0.015 0.034 0.058 0.078 0.11 0.18 0.060 2.3 in % 0.2 3.2 6.6 0.5 4.5 5.5 1.9 2.0